Structural performance of a 26-year-old corroded reinforced concrete beam
Résumé
This article presents experimental results and the modelling of a highly corroded beam subjected to a chloride environment to assess the performance of long-term-corrosion-damaged beams. A reinforced concrete beam corroded by 26 years of exposure to a chloride environment was tested until failure, as was a control beam of the same age. Cracking maps and corrosion maps were drawn for the corroded beam. Force displacement curves for both beams and stress strain curves for the steel bars were also plotted. From the results it appears that corrosion has a significant impact on the load carrying capacity, stiffness and deflection of beams. The modelling approach using Macro Finite Element (MFE) shows good agreement with experimental results in terms of load capacity, stiffness of the beam and ultimate deflection.
Cet article présente les résultats expérimentaux et la modélisation du comportement mécanique d’une poutre sévèrement corrodée par 26 années de conservation en atmosphère saline. Après avoir été testée en flexion jusqu’à la rupture, la poutre a été désossée afin de déterminer la carte de corrosion des armatures et de faire des tests de traction sur les armatures corrodées. Les résultats montrent que la corrosion des armatures a une influence importante sur la capacité portante, la raideur en service et la ductilité (flèche à rupture) L’approche de modélisation par macro-élement montre une bonne corrélation en terme de charge ultime, raideur et déplacement maximal.